Three-dimensional printing with pore promoting compounds

ABSTRACT

The present disclosure describes kits and compositions for three dimensional printing, systems for three-dimensional printing, and methods of making three-dimensional printed articles. In one example, a multi-fluid kit for three-dimensional printing comprises: a fusing agent comprising water and a radiation absorber, wherein the radiation absorber absorbs radiation energy and converts the radiation energy to heat; and a pore-promoting agent comprising water and a water-soluble pore-promoting compound, wherein the pore promoting compound chemically reacts at an elevated temperature to generate a gas, and wherein the water-soluble pore-promoting compound is selected from the group consisting of sodium bicarbonate, potassium bicarbonate, and combinations thereof.

CROSS-REFERENCE TO RELATED APPLICATIONS

This patent application claims priority to PCT/US2019/036229 filed on Jun. 10, 2019 and incorporates this application in its entirety herein.

BACKGROUND

Methods of three-dimensional (3D) digital printing, a type of additive manufacturing, have continued to be developed over the last few decades. However, systems for 3D printing have historically been very expensive, though those expenses have been coming down to more affordable levels recently. In general, 3D printing technology can shorten the product development cycle by allowing rapid creation of prototype models for reviewing and testing. Unfortunately, the concept has been somewhat limited with respect to commercial production capabilities because the range of materials used in 3D printing is likewise limited. Accordingly, it can be difficult to 3D print functional parts with desired properties such as mechanical strength, visual appearance, and so on. Nevertheless, several commercial sectors such as aviation and the medical industry have benefitted from the ability to rapidly prototype and customize parts for customers.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic view of an example multi-fluid kit for three-dimensional printing in accordance with examples of the present disclosure,

FIG. 2 is a schematic view of another example multi-fluid kit for three-dimensional printing in accordance with examples of the present disclosure.

FIG. 3 is a schematic view of an example three-dimensional printing kit in accordance with examples of the present disclosure.

FIGS. 4A-4C show a schematic view of an example three-dimensional printing process using an example multi-fluid kit in accordance with examples of the present disclosure.

FIG. 5 is a flowchart illustrating an example method of making a three-dimensional printed article in accordance with examples of the present disclosure.

FIGS. 6A-6B show an example three-dimensional printed article and a cross-section of the three-dimensional printed article in accordance with examples of the present disclosure.

FIGS. 7A-7B show another example three-dimensional printed article and a cross-section of the three-dimensional printed article in accordance with examples of the present disclosure.

The figures depict examples of the presently disclosed technology. However, it should be understood that the present technology is not limited to the examples depicted.

DETAILED DESCRIPTION

A way to modulate mechanical properties of a 3D printed part or additive manufactured part without changing the polymer build material can include use of specific agents and/or manufacturing methods. While the foregoing can offer the ability to alter mechanical properties of 3D printed parts, there are still constraints around feature sizes being accessible by jetting.

Prior solutions have included incorporation of lattice/pore-like structures into mechanical design of the part via digital means (with inherent limitations being present regarding what feature sizes can be produced by the 3DP process itself—i.e., design-assisted porosity can only be as small as the 3DP process accuracy allows). Another prior solution involves use of urea directly in the fusing agent to generate gaseous products.

The 3D printing methods, systems, kits, and compositions disclosed herein allow generating of parts by 3D printing with porous cores and solid outer shells without trapped powder. This can be accomplished by enabling in situ gas generation during the build process, spatial control over pore density, and location can be achieved.

The onset temperature of sodium bicarbonate and/or potassium bicarbonate to generate carbon dioxide, however, is significantly lower than urea and enables greater versatility for pore generation on a wider variety of different materials.

In one example, described herein is a multi-fluid kit for three-dimensional printing comprising: a fusing agent comprising water and a radiation absorber, wherein the radiation absorber absorbs radiation energy and converts the radiation energy to heat; and a pore-promoting agent comprising water and a water-soluble pore-promoting compound, wherein the pore-promoting compound chemically reacts at an elevated temperature to generate a gas, and wherein the water-soluble pore-promoting compound is selected from the group consisting of sodium bicarbonate, potassium bicarbonate, and combinations thereof.

In some examples, the pore-promoting compound is sodium bicarbonate.

In some examples, the pore-promoting compound is present in an amount from about 1 wt % to about 10 wt % with respect to the total weight of the pore-promoting agent.

In some examples, the elevated temperature at which the pore-promoting compound chemically reacts is from about 80° C. to about 200° C.

In some examples, the radiation absorber is a metal dithiolene complex, carbon black, a near-infrared absorbing dye, a near-infrared absorbing pigment, metal nanoparticles, a conjugated polymer, or a combination thereof.

In some examples, the multi-fluid kit can further comprises a detailing agent comprising a detailing compound, wherein the detailing compound reduces a temperature of powder bed material onto which the detailing agent is applied.

In one example, described herein is a three-dimensional printing kit comprising: a powder bed material comprising polymer particles; a fusing agent comprising water and a radiation absorber to selectively apply to the powder bed material, wherein the radiation absorber absorbs radiation energy and converts the radiation energy to heat; and a pore-promoting agent comprising water and a water-soluble pore-promoting compound, wherein the pore-promoting compound chemically reacts at an elevated temperature to generate a gas, and wherein the water-soluble pore-promoting compound is selected from the group consisting of sodium bicarbonate, potassium bicarbonate, and combinations thereof.

In some examples, the polymer particles have an average particle size from about 20 μm to about 100 μm and include polyamide-6, polyamide-9, polyamide-11, polyamide-12, polyamide-6,6, polyamide-6,12, polyethylene, thermoplastic polyurethane, thermoplastic polyamide, polypropylene, polyester, polycarbonate, polyether ketone, polyacrylate, polystyrene powder, wax, or a combination thereof.

In some examples, the pore-promoting compound is sodium bicarbonate.

In some examples, the radiation absorber is a metal dithiolene complex, carbon black, a near-infrared absorbing dye, a near-infrared absorbing pigment, metal nanoparticles, a conjugated polymer, or a combination thereof.

In some examples, the elevated temperature at which the pore-promoting compound chemically reacts is from about 80° C. to about 200° C.

In one example, described herein is a method of three-dimensional printing comprising: iteratively applying individual build material layers of polymer particles to a powder bed; based on a three-dimensional object model, selectively jetting a fusing agent onto the individual build material layers, wherein the fusing agent comprises water and a radiation absorber; based on the three-dimensional object model selectively jetting a pore-promoting agent onto the individual build material layers, wherein the pore-promoting agent comprises water and a water-soluble pore-promoting compound, wherein the pore-promoting compound chemically reacts at an elevated temperature to generate a gas, and wherein the water-soluble pore-promoting compound is selected from the group consisting of sodium bicarbonate, potassium bicarbonate, and combinations thereof; and exposing the powder bed to energy to selectively fuse the polymer particles in contact with the radiation absorber to form a fused polymer matrix at individual build material layers, thereby heating the pore-promoting compound to the elevated temperature to generate the gas distributed in the fused polymer matrix.

In some examples, the pore-promoting compound is sodium bicarbonate.

In some examples, the elevated temperature is from about 80° C. to about 200° C.

In some examples, the gas forms isolated pores in the fused polymer matrix, the pores having an average diameter from about 0.1 micrometer to about 100 micrometers.

The multi-fluid kits, materials kits, and methods described herein can be used to make three-dimensional (3D) printed articles that are porous or that have porous portions. In particular methods that involve 3D printing using a powder bed of polymer powder, a pore-promoting agent can be selectively applied to the powder bed. A fusing agent can also be selectively applied to the powder bed. Generally, the fusing agent can include a radiation absorber that can absorb radiation and convert the radiation to heat. After applying the fusing agent and the pore-promoting agent, the powder bed can be exposed to radiation. Portions of the powder bed where the fusing agent was applied can heat up to the point that the polymer powder can becomes fused together to form a solid layer. At the same time, the heat can cause the pore-promoting compound in the pore-promoting agent to react and form a gas.

In some examples, the gas can become trapped as small bubbles in the molten polymer. When the polymer hardens, the bubbles can remain as pores within the polymer matrix. In some cases, the pore-promoting agent can be applied in the same areas as the fusing agent to make a 3D printed article that has uniform porosity throughout the article. In other examples, the pore-promoting agent can be printed on a limited portion of the area where the fusing agent was printed. This can form a 3D printed article that has a porous portion and a non-porous portion. Any size, shape, and number of porous portions can be designed and produced in the 3D printed article by selectively applying the pore-promoting agent.

Forming 3D printed articles with porosity as described herein can be difficult using many 3D printing methods. In methods that use a powder bed, forming a 3D printed article with internal closed pores is not ideal because powder build material can become trapped inside the pores with no way to remove the powder after printing the article. Additionally, methods of 3D printing using powder build material are usually limited as to the size of features that can be formed by the printing resolution of the process. For example, a 3D printing process that involves applying a fusing agent to a powder bed may be used to form pores by designing the pores into the 3D object model and then printing the article with pores according to the 3D object model. However, the printing resolution of such a process can be limited by the resolution at which the fusing agent is applied to the powder bed and the particle size of the powder build material. Therefore, explicitly designing and printing pores using such a process can be limited to pores that are larger than the print resolution.

In contrast, the methods and materials described herein can be used to form pores that are smaller than the print resolution of the 3D printing process. In some examples, the pores formed using these methods can be smaller than the particle size of the polymer powder build material.

Porosity formed using the methods described herein can affect the overall properties of the 3D printed article. For example, a 3D printed article can be made porous in order to reduce the weight of the article. In another example, porosity can be introduced with the intention of reducing the stiffness or strength of the article. In another example, porosity to can be used to manipulate crack propagation. In other words, porosity can also help determine how a crack might route/propagate through a part. A certain portion of the 3D printed article may be made porous to make that particular portion less stiff if desired. Thus, the ability to selectively form porous portions in 3D printed articles can be useful in a variety of applications.

Additionally, the methods described herein can allow for the extent of porosity to be controlled and tuned at temperatures that are lower than those for some compounds like urea. Lower temperatures allow for reduced oxidation of the polymer build material in the powder bed thereby reducing any unnecessary oxidation/yellowing issues at temperatures higher than 200° C. The pores are formed by a pore-promoting compound in the pore-promoting agent. The pore-promoting compound can be a compound that chemically reacts to form a gas when the compound is heated to an elevated temperature of from about 80° C. to about 200° C. The pore-promoting compound can be selected from the group consisting of sodium bicarbonate, potassium bicarbonate, and combinations thereof.

In some examples, the level of porosity in the 3D printed article can be adjusted by changing the amount of pore-promoting agent that is applied to the build material. In other examples, the level of porosity can be adjusted by changing the amount of heating provided to the pore-promoting compound. For example, the build material with the pore-promoting compound applied thereto can be exposed to more intense radiation or exposed for a longer time to supply more heat to the pore-promoting compound, and thereby cause more of the pore-promoting compound to react to form gas. Accordingly, the methods described herein provide multiple avenues for controlling the porosity level in the 3D printed article.

Multi-Fluid Kits

With this description in mind, FIG. 1 shows a schematic of an example multi-fluid kit for three-dimensional printing 100. The multi-fluid kit includes a fusing agent 110 and a pore-promoting agent 120. The fusing agent can include water and a radiation absorber. The radiation absorber can absorb radiation energy and convert the radiation energy to heat. The pore-promoting agent can include water and a water-soluble pore-promoting compound. As described above, the fusing agent can be applied to a powder bed material in areas that are to be fused to form a layer of a 3D printed article. The pore-promoting agent can be applied to areas of the powder bed where porosity is to be formed.

FIG. 2 shows a schematic of another example multi-fluid kit for three-dimensional printing 200. This multi-fluid kit also includes a fusing agent 210 and a pore-promoting agent 220. Additionally, this multi-fluid kit includes a detailing agent 230. The detailing agent can include a detailing compound, which is a compound that can reduce the temperature of powder bed material onto which the detailing agent is applied. In some examples, the detailing agent can be applied around edges of the area where the fusing agent is applied. This can prevent powder bed material around the edges from caking due to heat from the area where the fusing agent was applied. The detailing agent can also be applied in the same area where fusing was applied in order to control the temperature and prevent excessively high temperatures when the powder bed material is fused.

Three-Dimensional Printing Kits

The present disclosure also describes materials kit for three-dimensional printing. In some examples, the materials kits can include materials that can be used in the three-dimensional printing processes described herein. FIG. 3 shows a schematic illustration of one example three-dimensional printing kit 300 in accordance with examples of the present disclosure. The kit includes a powder bed material 340 including polymer particles, a fusing agent 310 to selectively apply to the powder bed material, and a pore-promoting agent 320 to selectively apply to the powder bed material. The pore-promoting agent includes a pore-promoting compound, which can be a compound that chemically reacts to form a gas when the compound is heated to an elevated temperature of from about 80° C. to about 200° C. The pore-promoting compound can be selected from the group consisting of sodium bicarbonate, potassium bicarbonate, and combinations thereof.

Three-Dimensional Printing Methods

FIGS. 4A-4C illustrate one example of using the multi-fluid kits to form a 3D printed article. In FIG. 4A, a fusing agent 310 and a pore-promoting agent 320 are jetted onto a layer of powder bed material 340 including polymer particles. The fusing agent is jetted from a fusing agent ejector 312 and the pore-promoting agent is jetted from a pore-promoting agent ejector 322. These fluid ejectors can move across the layer of polymer particles to selectively jet fusing agent on areas that are to be fused, while the pore-promoting agent can be jetted onto areas that are to be made porous. If a detailing agent were to be used, there may be an additional detailing agent ejector (not shown) that contains detailing agent to be applied at or about boundary areas of the three-dimensional article being printed. Furthermore, a radiation source 352 can also move across the layer of polymer particles.

FIG. 4B shows the layer of powder bed material 340, which includes polymer particles, after the fusing agent 310 has been jetted onto an area of the layer that is to be fused. Additionally, the pore-promoting agent 320 has been jetted onto a portion of the area where the fusing agent was also jetted. In this figure, the radiation source 352 is shown emitting radiation 350 toward the layer of polymer particles. The fusing agent can include a radiation absorber that can absorb this radiation and convert the radiation energy to heat,

FIG. 4C shows the layer of powder bed material 340 including polymer particles with a fused portion 342 where the fusing agent was jetted. This portion has reached a sufficient temperature to fuse the polymer particles together to form a solid polymer matrix. The area where the pore-promoting agent was jetted becomes a porous portion 344. This portion includes many pores formed when the pore-promoting compound in the pore-promoting agent reacted to form gas when heated. The reaction formed gas bubbles in the molten polymer, and gas bubbles became trapped when the polymer re-solidified to form the solid polymer matrix.

As used herein, “pores” refers to void spaces in the solid polymer matrix. The void spaces may be individual, closed void spaces that are separated from other void spaces by solid polymer. In other examples, the void spaces may be interconnected with other void spaces. Thus, in various examples, depending on the extent of porosity, the pores can range from a fully interconnected network of voids to a collection of discrete, unconnected voids. In further examples, the void spaces can be filled by gas that is generated by a chemical reaction of the pore-promoting compound.

As used herein, “porosity” in a general context can refer to the present of pores in the fused polymer matrix. In the context of a specific value, “porosity” can be defined as the volume fraction of void space in the fused polymer with respect to the entire volume of the fused polymer together with the void space. The void space can refer to voids formed by the chemical reaction of the pore-promoting compound, and not void spaces designed into the 3D model for 3D printing the article in question. Any geometry designed into the 3D object model can be considered features of the “entire volume of the fused polymer” and the fraction of void space can be based on the voids formed by gas generated by the pore-promoting compound. Additionally, porosity can be measured with respect to the entire 3D printed article or with respect to a porous portion of the 3D printed article (where the pore-promoting agent was applied).

In some examples, a porous portion of a 3D printed article made using the methods described herein can have a porosity from about 0.1 vol % to about 50 vol %. In further examples, the porous portion can have a porosity from about 1 vol % to about 30 vol % or from about 5 vol % to about 20 vol %. Additionally, the size of the pores can vary. In some examples, the pores can have an average diameter from about 1 micrometer to about 500 micrometers. In further examples, the pores can have an average diameter from about 2 micrometers to about 300 micrometers or from about 5 micrometers to about 50 micrometers.

Powder Bed Material

In certain examples, the powder bed material can include polymer particles having a variety of shapes, such as substantially spherical particles or irregularly-shaped particles. In some examples, the polymer powder can be capable of being formed into 3D printed objects with a resolution of about 20 μm to about 100 μm, about 30 μm to about 90 μm, or about 40 μm to about 80 μm. As used herein. “resolution” refers to the size of the smallest feature that can be formed on a 3D printed object. The polymer powder can form layers from about 20 μm to about 100 μm thick, allowing the fused layers of the printed part to have roughly the same thickness. This can provide a resolution in the z-axis (i.e., depth) direction of about 20 μm to about 100 μm. The polymer powder can also have a sufficiently small particle size and sufficiently regular particle shape to provide about 20 μm to about 100 μm resolution along the x-axis and y-axis (i.e., the axes parallel to the top surface of the powder bed). For example, the polymer powder can have an average particle size from about 20 μm to about 100 μm. In other examples, the average particle size can be from about 20 μm to about 50 μm. Other resolutions along these axes can be from about 30 μm to about 90 μm or from 40 μm to about 80 μm.

The polymer powder can have a melting or softening point from about 70° C. to about 350° C. In further examples, the polymer can have a melting or softening point from about 150° C. to about 200° C. A variety of thermoplastic polymers with melting points or softening points in these ranges can be used. For example, the polymer powder can be polyamide-6 powder, polyamide-9 powder, polyamide-11 powder, polyamide-12 powder, polyamide-6,6 powder, polyamide-6,12 powder, polyethylene powder, wax, thermoplastic polyurethane powder, thermoplastic polyamide, acrylonitrile butadiene styrene powder, amorphous polyamide powder, polymethylmethacrylate powder, ethylene-vinyl acetate powder, polyarylate powder, silicone rubber, polypropylene powder, polyester powder, polycarbonate powder, copolymers of polycarbonate with acrylonitrile butadiene styrene, copolymers of polycarbonate with polyethylene terephthalate polyether ketone powder, polyacrylate powder, polystyrene powder, or mixtures thereof. In a specific example, the polymer powder can be thermoplastic polyamide, which can have a melting point from about 100° C. to about 140° C. In another specific example, the polymer powder can be polyamide-12, which can have a melting point from about 155° C. to about 185° C.

The thermoplastic polymer particles can also in some cases be blended with a filler. The filler can include inorganic particles such as alumina, silica, fibers, carbon nanotubes, or combinations thereof. When the thermoplastic polymer particles fuse together, the filler particles can become embedded in the polymer, forming a composite material. In some examples, the filler can include a free-flow agent, anti-caking agent, or the like. Such agents can prevent packing of the powder particles, coat the powder particles and smooth edges to reduce inter-particle friction, and/or absorb moisture. In some examples, a weight ratio of thermoplastic polymer particles to filler particles can be from about 100:1 to about 1:2 or from about 5:1 to about 1:1.

Fusing Agents

The multi-fluid kits and materials kits for three-dimensional printing described herein can include a fusing agent to be applied to the polymer build material. The fusing agent can include a radiation absorber that can absorb radiant energy and convert the energy to heat. In certain examples, the fusing agent can be used with a powder bed material in a particular 3D printing process. A thin layer of powder bed material can be formed, and then the fusing agent can be selectively applied to areas of the powder bed material that are desired to be consolidated to become part of the solid 3D printed object. The fusing agent can be applied, for example, by printing such as with a fluid ejector or fluid jet printhead. Fluid jet printheads can jet the fusing agent in a similar way to an inkjet printhead jetting ink. Accordingly, the fusing agent can be applied with great precision to certain areas of the powder bed material that are desired to form a layer of the final 3D printed object. After applying the fusing agent, the powder bed material can be irradiated with radiant energy. The radiation absorber from the fusing agent can absorb this energy and convert it to heat, thereby heating any polymer particles in contact with the radiation absorber. An appropriate amount of radiant energy can be applied so that the area of the powder bed material that was printed with the fusing agent heats up enough to melt the polymer particles to consolidate the particles into a solid layer, while the powder bed material that was not printed with the fusing agent remains as a loose powder with separate particles.

In some examples, the amount of radiant energy applied, the amount fusing agent applied to the powder bed, the concentration of radiation absorber in the fusing agent, and the preheating temperature of the powder bed (i.e., the temperature of the powder bed material prior to printing the fusing agent and irradiating) can be tuned to ensure that the portions of the powder bed printed with the fusing agent will be fused to form a solid layer and the unprinted portions of the powder bed will remain a loose powder. These variables can be referred to as parts of the “print mode” of the 3D printing system. Generally, the print mode can include any variables or parameters that can be controlled during 3D printing to affect the outcome of the 3D printing process.

Generally, the process of forming a single layer by applying fusing agent and irradiating the powder bed can be repeated with additional layers of fresh powder bed material to form additional layers of the 3D printed article, thereby building up the final object one layer at a time. In this process, the powder bed material surrounding the 3D printed article can act as a support material for the object. When the 3D printing is complete, the article can be removed from the powder bed and any loose powder on the article can be removed.

Accordingly, in some examples, the fusing agent can include a radiation absorber that is capable of absorbing electromagnetic radiation to produce heat. The radiation absorber can be colored or colorless. In various examples, the radiation absorber can be a pigment such as carbon black pigment, glass fiber, titanium dioxide, clay, mica, talc, barium sulfate, calcium carbonate, a near-infrared absorbing dye, a near-infrared absorbing pigment, a conjugated polymer, a dispersant, or combinations thereof. Examples of near-infrared absorbing dyes include aminium dyes, tetraaryldiamine dyes, cyanine dyes, pthalocyanine dyes, dithiolene dyes, and others. In further examples, radiation absorber can be a near-infrared absorbing conjugated polymer such as poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS), a polythiophene, poly(p-phenylene sulfide), a polyaniline, a poly(pyrrole), a poly(acetylene), poly(p-phenylene vinylene), polyparaphenylene, or combinations thereof. As used herein, “conjugated” refers to alternating double and single bonds between atoms in a molecule. Thus, “conjugated polymer” refers to a polymer that has a backbone with alternating double and single bonds. In many cases, the radiation absorber can have a peak absorption wavelength in the range of about 800 nm to about 1400 nm.

A variety of near-infrared pigments can also be used. Non-limiting examples can include phosphates having a variety of counterions such as copper, zinc, iron, magnesium, calcium, strontium, the like, and combinations thereof. Non-limiting specific examples of phosphates can include M₂P₂O₇, M₄P₂O₉, M₅P₂O₁₀, M₃(PO₄)₂, M(PO₃)₂, M₂P₄O₁₂, and combinations thereof, where M represents a counterion having an oxidation state of +2, such as those listed above or a combination thereof. For example, M₂P₂O₇ can include compounds such as Cu₂P₂O₇, Cu/MgP₂O₇, Cu/ZnP₂O₇, or any other suitable combination of counterions. It is noted that the phosphates described herein are not limited to counterions having a +2 oxidation state. Other phosphate counterions can also be used to prepare other suitable near-infrared pigments.

Additional near-infrared pigments can include silicates. Silicates can have the same or similar counterions as phosphates. One non-limiting example can include M₂SiO₄, M₂Si₂O₆, and other silicates where M is a counterion having an oxidation state of +₂. For example, the silicate M₂Si₂O₆ can include Mg₂Si₂O₆, Mg/CaSi₂O₆, MgCuSi₂O₆, Cu₂Si₂O₆, Cu/ZnSi₂O₆, or other suitable combination of counterions. It is noted that the silicates described herein are not limited to counterions having a +2 oxidation state. Other silicate counterions can also be used to prepare other suitable near-infrared pigments.

In further examples, the radiation absorber can include a metal dithiolene complex. Transition metal dithiolene complexes can exhibit a strong absorption band in the 600 nm to 1600 nm region of the electromagnetic spectrum. In some examples, the central metal atom can be any metal that can form square planer complexes. Non-limiting specific examples include complexes based on nickel, palladium, and platinum.

A dispersant can be included in the fusing agent in some examples. Dispersants can help disperse the radiation absorbing pigments described above. In some examples, the dispersant itself can also absorb radiation. Non-limiting examples of dispersants that can be included as a radiation absorber, either alone or together with a pigment, can include polyoxyethylene glycol octylphenol ethers, ethoxylated aliphatic alcohols, carboxylic esters, polyethylene glycol ester, anhydrosorbitol ester, carboxylic amide, polyoxyethylene fatty acid amide, poly (ethylene glycol) p-isooctyl-phenyl ether, sodium polyacrylate, and combinations thereof.

The amount of radiation absorber in the fusing agent can vary depending on the type of radiation absorber. In some examples, the concentration of radiation absorber in the fusing agent can be from about 0.1 wt % to about 20 wt %. In one example, the concentration of radiation absorber in the fusing agent can be from about 0.1 wt % to about 15 wt %. In another example, the concentration can be from about 0.1 wt % to about 8 wt %. In yet another example, the concentration can be from about 0.5 wt % to about 2 wt %. In a particular example, the concentration can be from about 0.5 wt % to about 1.2 wt %. In one example, the radiation absorber can have a concentration in the fusing agent such that after the fusing agent is jetted onto the polymer powder, the amount of radiation absorber in the polymer powder can be from about 0.0003 wt % to about 10 wt %, or from about 0.005 wt % to about 5 wt %, with respect to the weight of the polymer powder.

In some examples, the fusing agent can be jetted onto the polymer powder build material using a fluid jetting device, such as inkjet printing architecture. Accordingly, in some examples, the fusing agent can be formulated to give the fusing agent good jetting performance. Ingredients that can be included in the fusing agent to provide good jetting performance can include a liquid vehicle. Thermal jetting can function by heating the fusing agent to form a vapor bubble that displaces fluid around the bubble, and thereby forces a droplet of fluid out of a jet nozzle. Thus, in some examples the liquid vehicle can include a sufficient amount of an evaporating liquid that can form vapor bubbles when heated. The evaporating liquid can be a solvent such as water, an alcohol, an ether, or a combination thereof.

In some examples, the liquid vehicle formulation can include a co-solvent or co-solvents present in total at from about 1 wt % to about 50 wt %, depending on the jetting architecture. Further, a non-ionic, cationic, and/or anionic surfactant can be present, ranging from about 0.01 wt % to about 5 wt %. In one example, the surfactant can be present in an amount from about 1 wt % to about 5 wt %. The liquid vehicle can include dispersants in an amount from about 0.5 wt % to about 3 wt %. The balance of the formulation can be purified water, and/or other vehicle components such as biocides, viscosity modifiers, materials for pH adjustment, sequestering agents, preservatives, and the like. In one example, the liquid vehicle can be predominantly water.

In some examples, a water-dispersible or water-soluble radiation absorber can be used with an aqueous vehicle. Because the radiation absorber is dispersible or soluble in water, an organic co-solvent may not be present, as it may not be included to solubilize the radiation absorber. Therefore, in some examples the fluids can be substantially free of organic solvent, e.g., predominantly water. However, in other examples a co-solvent can be used to help disperse other dyes or pigments, or enhance the jetting properties of the respective fluids. In still further examples, a non-aqueous vehicle can be used with an organic-soluble or organic-dispersible fusing agent.

In certain examples, a high boiling point co-solvent can be included in the fusing agent. The high boiling point co-solvent can be an organic co-solvent that boils at a temperature higher than the temperature of the powder bed during printing. In some examples, the high boiling point co-solvent can have a boiling point above about 250° C. In still further examples, the high boiling point co-solvent can be present in the fusing agent at a concentration from about 1 wt % to about 4 wt %.

Classes of co-solvents that can be used can include organic co-solvents including aliphatic alcohols, aromatic alcohols, diols, glycol ethers, polyglycol ethers, caprolactams, formamides, acetamides, and long chain alcohols. Examples of such compounds include 1-aliphatic alcohols, secondary aliphatic alcohols, 1,2-alcohols, 1,3-alcohols, 1,5-alcohols, ethylene glycol alkyl ethers, propylene glycol alkyl ethers, higher homologs (C₆-C₁₂) of polyethylene glycol alkyl ethers, N-alkyl caprolactams, unsubstituted caprolactams, both substituted and unsubstituted formamides, both substituted and unsubstituted acetamides, and the like. Specific examples of solvents that can be used include, but are not limited to, 2-pyrrolidinone, N-methylpyrrolidone, 2-hydroxyethyl-2-pyrrolidone, 2-methyl-1,3-propanediol, tetraethylene glycol, 1,6-hexanediol, 1,5-hexanediol and 1,5-pentanediol.

Regarding the surfactant that may be present, a surfactant or surfactants can be used, such as alkyl polyethylene oxides, alkyl phenyl polyethylene oxides, polyethylene oxide block copolymers, acetylenic polyethylene oxides, polyethylene oxide (di)esters, polyethylene oxide amines, protonated polyethylene oxide amines, protonated polyethylene oxide amides, dimethicone copolyols, substituted amine oxides, and the like. The amount of surfactant added to the fusing agent may range from about 0.01 wt % to about 20 wt %. Suitable surfactants can include, but are not limited to, liponic esters such as Tergitol™ 15-S-12, Tergitol™ 15-S-7 available from Dow Chemical Company (Michigan), LEG-1 and LEG-7; Triton™ X-100; Titon™ X-405 available from Dow Chemical Company (Michigan); and sodium dodecylsulfate.

Various other additives can be employed to enhance certain properties of the fusing agent for specific applications. Examples of these additives are those added to inhibit the growth of harmful microorganisms. These additives may be biocides, fungicides, and other microbial agents, which can be used in various formulations. Examples of suitable microbial agents include, but are not limited to, NUOSEPT® (Nudex, Inc., New Jersey), UCARCIDE™ (Union carbide Corp., Texas), VANCIDE® (R.T. Vanderbilt Co., Connecticut), PROXEL® (ICI Americas, New Jersey), and combinations thereof.

Sequestering agents, such as EDTA (ethylene diamine tetra acetic acid), may be included to eliminate the deleterious effects of heavy metal impurities, and buffer solutions may be used to control the pH of the fluid. From about 0.01 wt % to about 2 wt %, for example, can be used. Viscosity modifiers and buffers may also be present, as well as other additives to modify properties of the fluid as desired. Such additives can be present at from about 0.01 wt % to about 20 wt %.

Pore-Promoting Agents

The pore-promoting agent can include a water-soluble pore-promoting compound that can chemically react at an elevated temperature to generate a gas. As used herein, “chemically react” refers to a change in chemical composition and not a mere phase change from liquid or solid to gas. Many liquid solvents can evaporate to form a gas at an elevated temperature. However, the pore-promoting compound described herein does not refer to a liquid that evaporates at the elevated temperature. Instead, the pore-promoting compound undergoes a chemical reaction to form a different compound. The product of this chemical reaction can be a gas, and the gas can remain in a gaseous state even after cooling back to room temperature. In some examples, the chemical reaction of the pore-promoting compound can proceed without any other reactants besides the pore-promoting compound. In certain examples, the pore-promoting compound can chemically decompose to form smaller molecules, and the product molecules can include a gas.

Non-limiting examples of pore-promoting compounds can include sodium bicarbonate, potassium bicarbonate, and combinations thereof. These compounds can chemically decompose to form a gas when heated to a decomposition temperature of from about 80° C. to about 200° C. In some examples, the gas formed can include carbon dioxide gas.

In some examples, the pore-promoting agent can react to form a gas at an elevated temperature that is reached during the 3D printing process. In some examples, the elevated temperature at which the pore-promoting compound reacts can be from about 80° C. to about 200° C. In further examples, the elevated temperature can be from about 90° C. to about 190° C. or from about 100° C. to about 180° C. In certain examples, the elevated temperature can be at or near the melting or softening point temperature of the polymer particles in the powder bed. For example, the elevated temperature can be within 20° C., within 15° C., or within 10° C. of the melting or softening point of the polymer particles. Thus the pore-promoting compound can react when the polymer particles are fused during the 3D printing process. In other examples, the elevated temperature at which the pore-promoting reacts can be higher than the melting or softening point of the polymer particles. During the 3D printing process, a sufficient amount of fusing agent can be applied to the polymer particles and a sufficient amount of radiation energy can be applied to heat the pore-promoting compound to the temperature at which the pore-promoting compound will react.

In some cases, the pore-promoting compound that is applied to the powder bed can react completely to form gas when the powder bed is heated during fusing of the polymer particles. In other words, all or nearly all of the pore-promoting compound can react to yield the gas. In other examples, a portion of the pore-promoting compound can react and another portion can remain unreacted. In certain examples, from about 50 wt % to about 100 wt % of the pore-promoting compound can react. In other examples, from about 60 wt % to about 95 wt % or from about 70 wt % to about 90 wt % of the pore-promoting compound can react. In still further examples, less of the pore-promoting compound can react. For example, from about 10 wt % to about 70 wt %, or from about 20 wt % to about 60 wt %, or from about 30 wt % to about 50 wt % of the pore-promoting compound can react. The amount of the pore-promoting compound that reacts can in some cases depend on the temperature to which the powder bed is heated, the length of time that the powder is held at that temperature, the total amount of radiation energy applied to the powder bed, and so on. Accordingly, in some examples, the amount of radiation energy applied, the length of time that the powder bed is heated, to temperature reached by the powder bed, the amount of fusing agent applied to the powder bed, and other variables can affect the extent of the reaction of the pore-promoting compound. Therefore, these variables can affect the porosity of the final 3D printed article. These variables can be parts of the “print mode” of the 3D printing process. The porosity can also be affected by changing the amount of pore-promoting agent that is applied to the powder bed. Accordingly, the print mode can be adjusted to affect the level of porosity in the 3D printed article.

The total amount of pore-promoting compound that is present in the powder bed can directly affect the porosity of the 3D printed article. As mentioned above, this variable can be adjusted by changing the amount of pore-promoting agent that is applied to the powder bed. Alternatively, the amount of pore-promoting compound applied to the powder bed can be changed by changing the concentration of pore-promoting compound in the pore-promoting agent. The amount of pore-promoting compound can be selected to allow the pore-promoting agent to be jettable from a fluid jet printhead. In certain examples, the concentration of the pore-promoting compound in the pore-promoting agent can be from about 0.5 wt % to about 10 wt % with respect to the total weight of the pore-promoting agent. In further examples, the concentration of pore-promoting compound can be from 1 wt % to 8 wt % or from 2 wt % to 7 wt %.

The pore-promoting agent can also include ingredients to allow the pore-promoting agent to be jetted by a fluid jet printhead. In some examples, the pore-promoting agent can include jettability imparting ingredients such as those in the fusing agent described above. These ingredients can include a liquid vehicle, surfactant, dispersant, co-solvent, biocides, viscosity modifiers, materials for pH adjustment, sequestering agents, preservatives, and so on. These ingredients can be included in any of the amounts described above.

Detailing Agents

In further examples, multi-fluid kits or materials kits for three-dimensional printing can include a detailing agent. The detailing agent can include a detailing compound. The detailing compound can be capable of reducing the temperature of the powder bed material onto which the detailing agent is applied. In some examples, the detailing agent can be printed around the edges of the portion of the powder that is printed with the fusing agent. The detailing agent can increase selectivity between the fused and unfused portions of the powder bed by reducing the temperature of the powder around the edges of the portion to be fused.

In some examples, the detailing compound can be a solvent that evaporates at the temperature of the powder bed. In some cases the powder bed can be preheated to a preheat temperature within about 10° C. to about 70° C. of the fusing temperature of the polymer powder. Depending on the type of polymer powder used, the preheat temperature can be in the range of about 90° C. to about 200° C. or more. The detailing compound can be a solvent that evaporates when it comes into contact with the powder bed at the preheat temperature, thereby cooling the printed portion of the powder bed through evaporative cooling. In certain examples, the detailing agent can include water, co-solvents, or combinations thereof. Non-limiting examples of co-solvents for use in the detailing agent can include xylene, methyl isobutyl ketone, 3-methoxy-3-methyl-1-butyl acetate, ethyl acetate, butyl acetate, propylene glycol monomethyl ether, ethylene glycol mono tert-butyl ether, dipropylene glycol methyl ether, diethylene glycol butyl ether, ethylene glycol monobutyl ether, 3-methoxy-3-methyl-1-butanol, isobutyl alcohol, 1,4-butanediol, N,N-dimethyl acetamide, and combinations thereof. In some examples, the detailing agent can be mostly water. In a particular example, the detailing agent can be about 85 wt % water or more. In further examples, the detailing agent can be about 95 wt % water or more. In still further examples, the detailing agent can be substantially devoid of radiation absorbers. That is, in some examples, the detailing agent can be substantially devoid of ingredients that absorb enough radiation energy to cause the powder to fuse. In certain examples, the detailing agent can include colorants such as dyes or pigments, but in small enough amounts that the colorants do not cause the powder printed with the detailing agent to fuse when exposed to the radiation energy.

The detailing agent can also include ingredients to allow the detailing agent to be jetted by a fluid jet printhead. In some examples, the detailing agent can include jettability imparting ingredients such as those in the fusing agent described above. These ingredients can include a liquid vehicle, surfactant, dispersant, co-solvent, biocides, viscosity modifiers, materials for pH adjustment, sequestering agents, preservatives, and so on. These ingredients can be included in any of the amounts described above.

Methods of Making 3D Printed Articles

The present disclosure also describes methods of making three-dimensional printed articles. FIG. 5 shows a flowchart illustrating one example method 500 of making a three-dimensional printed article. The method includes: iteratively applying individual build material layers of polymer particles to a powder bed 510; based on a three-dimensional object model, selectively jetting a fusing agent onto the individual build material layers, wherein the fusing agent includes water and a radiation absorber 520; based on the three-dimensional object model selectively jetting a pore-promoting agent onto the individual build material layers, wherein the pore-promoting agent includes water and a water-soluble pore-promoting compound, wherein the pore-promoting compound chemically reacts at an elevated temperature to generate a gas 530; and exposing the powder bed to energy to selectively fuse the polymer particles in contact with the radiation absorber to form a fused polymer matrix at individual build material layers, thereby heating the pore-promoting compound to the elevated temperature to generate the gas distributed in the fused polymer matrix 540. The polymer particles, fusing agent, and pore-promoting agent can have any of the ingredients and properties described above.

The pore-promoting agent includes a pore-promoting compound, which can be a compound that chemically reacts to form a gas when the compound is heated to an elevated temperature of from about 80° C. to about 200° C. The pore-promoting compound can be selected from the group consisting of sodium bicarbonate, potassium bicarbonate, and combinations thereof.

In some examples, a detailing agent can also be jetted onto the powder bed. As described above, the detailing agent can be a fluid that reduces the maximum temperature of the polymer powder on which the detailing agent is printed. In particular, the maximum temperature reached by the powder during exposure to electromagnetic energy can be less in the areas where the detailing agent is applied. In certain examples, the detailing agent can include a solvent that evaporates from the polymer powder to evaporatively cool the polymer powder. The detailing agent can be printed in areas of the powder bed where fusing is not desired. In particular examples, the detailing agent can be printed along the edges of areas where the fusing agent is printed. This can give the fused layer a clean, defined edge where the fused polymer particles end and the adjacent polymer particles remain unfused. In other examples, the detailing agent can be printed in the same area where the fusing agent is printed to control the temperature of the area to be fused. In certain examples, some areas to be fused can tend to overheat, especially in central areas of large fused sections. To control the temperature and avoid overheating (which can lead to melting and slumping of the build material), the detailing agent can be applied to these areas

As mentioned above, in some examples, the elevated temperature at which the pore-promoting compound chemically reacts can be from about 80° C. to about 200° C. The pore-promoting compound, and the powder bed material onto which the pore-promoting compound was jetted, can reach this elevated temperature when the radiation energy is applied to the powder bed. In some examples, the elevated temperature can be at or near the melting or softening point of the polymer particles in the powder bed. In other examples, the elevated temperature can be above or below the melting or softening point of the polymer particles. In any of these examples, the pore-promoting compound can be heated to a sufficient temperature to react and form a gas while the polymer particles are in a melted or softened state so that gas bubbles can form in the melted or softened polymer.

Also as mentioned above, a variety of variables of the “print mode” can be adjusted to affect the level of porosity in the 3D printed article. In some examples, the methods of making 3D printed articles can include adjusting these variables to modify the level of porosity. In certain examples, the variables can include the amount of fusing agent applied to the powder bed, the amount of pore-promoting agent applied to the powder bed, the thickness of individual layers of build material, the intensity and duration of radiation applied to the powder bed, the preheating temperature of the powder bed, and so on.

The fusing agent and pore-promoting agent can be jetted onto the powder bed using fluid jet print heads. The amount of pore-promoting agent jetted onto the powder can be calibrated based on the concentration of pore-promoting compound in the pore-promoting agent, the desired porosity of the resulting porous portion to be printed, among other factors. Similarly, the amount of the fusing agent used can be calibrated based the concentration of radiation absorber in the fusing agent, the level of fusing desired for the polymer particles, and other factors. In some examples, the amount of fusing agent printed can be sufficient to contact the radiation absorber with the entire layer of polymer powder. For example, if an individual layer of polymer powder is 100 microns thick, then the fusing agent can penetrate 100 microns into the polymer powder. Thus the fusing agent can heat the polymer powder throughout the entire layer so that the layer can coalesce and bond to the layer below. After forming a solid layer, a new layer of loose powder can be formed, either by lowering the powder bed or by raising the height of a powder roller and rolling a new layer of powder.

In some examples, the entire powder bed can be preheated to a temperature below the melting or softening point of the polymer powder. In one example, the preheat temperature can be from about 10° C. to about 30° C. below the melting or softening point. In another example, the preheat temperature can be within 50° C. of the melting of softening point. In a particular example, the preheat temperature can be from about 100° C. to about 120° C. and the polymer powder can be thermoplastic polyamide polymer powder. In another example, the preheat temperature can be about 90° C. to about 100° C. and the polymer powder can be thermoplastic polyurethane. Preheating can be accomplished with a lamp or lamps, an oven, a heated support bed, or other types of heaters. In some examples, the entire powder bed can be heated to a substantially uniform temperature.

The powder bed can be irradiated with a fusing lamp. Suitable fusing lamps for use in the methods described herein can include commercially available infrared lamps and halogen lamps. The fusing lamp can be a stationary lamp or a moving lamp. For example, the lamp can be mounted on a track to move horizontally across the powder bed. Such a fusing lamp can make multiple passes over the bed depending on the amount of exposure used to coalesce the individual printed layer. The fusing lamp can be configured to irradiate the entire powder bed with a substantially uniform amount of energy. This can selectively coalesce the printed portions with fusing agent leaving the unprinted portions of the polymer powder below the melting or softening point.

In one example, the fusing lamp can be matched with the radiation absorber in the fusing agent so that the fusing lamp emits wavelengths of light that match the peak absorption wavelengths of the radiation absorber. A radiation absorber with a narrow peak at a particular near-infrared wavelength can be used with a fusing lamp that emits a narrow range of wavelengths at approximately the peak wavelength of the radiation absorber. Similarly, a radiation absorber that absorbs a broad range of near-infrared wavelengths can be used with a fusing lamp that emits a broad range of wavelengths. Matching the radiation absorber and the fusing lamp in this way can increase the efficiency of coalescing the polymer particles with the fusing agent printed thereon, while the unprinted polymer particles do not absorb as much light and remain at a lower temperature.

Depending on the amount of radiation absorber present in the polymer powder, the absorbance of the radiation absorber, the preheat temperature, and the melting or softening point of the polymer, an appropriate amount of irradiation can be supplied from the fusing lamp. In some examples, the fusing lamp can irradiate individual layers for from about 0.5 to about 10 seconds per pass.

The 3D printed article can be formed by jetting a fusing agent onto layers of powder bed build material according to a 3D object model. 3D object models can in some examples be created using computer aided design (CAD) software. 3D object models can be stored in any suitable file format. In some examples, a 3D printed article as described herein can be based on a single 3D object model. The 3D object model can define the three-dimensional shape of the article and the three-dimensional shape of porous portions to be formed in the 3D printed article. In other examples, the article can be defined by a first 3D object model and the porous portions can be defined by a second 3D object model. Other information may also be included, such as structures to be formed of additional different materials or color data for printing the article with various colors at different locations on the article. The 3D object model may also include features or materials specifically related to jetting fluids on layers of powder bed material, such as the desired amount of fluid to be applied to a given area. This information may be in the form of a droplet saturation, for example, which can instruct a 3D printing system to jet a certain number of droplets of fluid into a specific area. This can allow the 3D printing system to finely control radiation absorption, cooling, color saturation, concentration of the pore-promoting compound, and so on. All this information can be contained in a single 3D object file or a combination of multiple files. The 3D printed article can be made based on the 3D object model. As used herein, “based on the 3D object model” can refer to printing using a single 3D object model file or a combination of multiple 3D object models that together define the article. In certain examples, software can be used to convert a 3D object model to instructions for a 3D printer to form the article by building up individual layers of build material.

In an example of the 3D printing process, a thin layer of polymer powder can be spread on a bed to form a powder bed. At the beginning of the process, the powder bed can be empty because no polymer particles have been spread at that point. For the first layer, the polymer particles can be spread onto an empty build platform. The build platform can be a flat surface made of a material sufficient to withstand the heating conditions of the 3D printing process, such as a metal. Thus, “applying individual build material layers of polymer particles to a powder bed” includes spreading polymer particles onto the empty build platform for the first layer. In other examples, a number of initial layers of polymer powder can be spread before the printing begins. These blank layers of powder bed material can in some examples number from about 10 to about 500, from about 10 to about 200, or from about 10 to about 100. In some cases, spreading multiple layers of powder before beginning the print can increase temperature uniformity of the 3D printed article. A fluid jet printing head, such as an inkjet print head, can then be used to print a fusing agent including a radiation absorber over portions of the powder bed corresponding to a thin layer of the 3D article to be formed. Then the bed can be exposed to electromagnetic energy, e.g., typically the entire bed. The electromagnetic energy can include light, infrared radiation, and so on. The radiation absorber can absorb more energy from the electromagnetic energy than the unprinted powder. The absorbed light energy can be converted to thermal energy, causing the printed portions of the powder to soften and fuse together into a formed layer. After the first layer is formed, a new thin layer of polymer powder can be spread over the powder bed and the process can be repeated to form additional layers until a complete 3D article is printed. Thus, “applying individual build material layers of polymer particles to a powder bed” also includes spreading layers of polymer particles over the loose particles and fused layers beneath the new layer of polymer particles.

In certain examples, the 3D printed article can be formed with porosity throughout the 3D printed article, or with a porous portion of any desired shaped located in any desired location within the 3D printed article. In one example, the 3D printed article can have a porous interior and a solid exterior surface. For example, the 3D printed article can be designed to have a solid layer or shell without any pore-promoting agent and then an interior portion where the pore-promoting agent is applied. In some examples, the solid shell can be from about 20 micrometers to about 2,000 micrometers thick, or any other desired thickness. In further examples, porosity can be formed in the 3D printed article for the purpose of reducing the weight of the article, increasing buoyancy of the article, decreasing strength of the article, increasing flexibility of the article, and so on. In one example, a certain portion of the article can be made highly porous to form a breakaway segment that can be snapped apart with moderate force. In another example, a portion of the article can be made porous while other portions are non-porous, to provide for a more flexible porous segment connected to more rigid non-porous segments. In yet another example, a hidden label, code, or identification mark can be formed using the pore-promoting agent. For example, a porous portion of a particular shaped can be formed in the interior of the 3D printed article beneath the surface, so that the porous portion is not visible to the human eye. The porous portion can be detected using detection equipment to find or read the hidden identification label or code. In this way, a porous label or code can be used to verify authenticity of a 3D printed article or to store information about the 3D printed article. Besides these examples, 3D printed articles with porous portions can be used for a variety of additional applications.

EXAMPLES

The following illustrates examples of the present disclosure. However, it is to be understood that the following are merely illustrative of the application of the principles of the present disclosure. Numerous modifications and alternative devices, methods, and systems may be devised without departing from the spirit and scope of the present disclosure. The appended claims are intended to cover such modifications and arrangements.

Example 1

5-10 wt % sodium bicarbonate containing pore-promoting agent formulations (see Table 1) were examined to print standard type 5 dogbones using PA-12. Fusing speeds ranged from 20×20 ips to 22×22 ips with a bed temperature set around 165° C. for PA-12. It is important to note that the sodium bicarbonate containing pore-promoting agent was incorporated by directly overlaying the agent over the fusing agent (see Table 2) throughout the build. A set of control dogbones were printed that directly overlaid triethylene glycol-free detailing agent (see Table 3) to ensure that significant porosity was not generated simply due to the presence of excess solvent, but due to the decomposition of sodium bicarbonate.

TABLE 1 Ingredient Concentration (wt %) Propylene glycol 5-30 Sodium bicarbonate 5-10 Tergitol ® 15-S-9 0.1-1   Deionized Water Balance

TABLE 2 Component Concentration (wt %) Near Infrared Absorber  5-12 Organic Solvent  15-25 Surfactant 0.1-5  Biocide 0.01-0.1 Complexing Agent 0.001-0.01 water Balance

TABLE 3 Component Concentration (wt %) Organic Solvent  10-20 Surfactant 0.5-1 Anti-kogation agent and 0.1-1 chelating agent Biocide 0.1-1 Colorant(s)   0-10 Water Balance

Example 2

To provide further experimental support, sodium bicarbonate agents were evaluated on thermoplastic polyamide polymer powder which has lower bed and melt temperatures (120° C.) than PA-12 (165° C.). The importance behind this experiment relies on the fact that gas generation, and therefore pore density, is a direct function of temperature. In general, the higher the bed temperature, the faster the rate of pore generation. It was demonstrated that porosity could be generated (see pores 610 shown in FIG. 6B) despite the lower bed temperature (of between about 100° C. and 140° C.) of thermoplastic polyamide with the pore-promoting agent of Table 4 when compared to the detailing agent control (no pores in FIG. 6A).

TABLE 4 Ingredient Concentration (wt %) Propylene glycol 25 Sodium bicarbonate 5 Tergitol ® 15-S-9 0.7 Deionized Water balance

Example 3

A comparison of the urea-based fusing agent and the sodium bicarbonate-based pore promoting agent was evaluated. Both urea and sodium bicarbonate were evaluated at 5 wt % concentration and jetted at equal ink densities (approximately 80 contone). The sodium bicarbonate pore-promoting agent composition is shown in Table 4 and the urea based fusing agent composition is shown in Table 5.

TABLE 5 Ingredient Concentration (wt %) Organic Co-solvent    5-30 High Boiling Point Solvent    1-10 Wetting Agent 0.01-1 Emulsifier 0.01-1 Chelating Agent 0.01-1 Biocide 0.01-1 Carbon Black Pigment    1-10 Deionized Water balance

Upon computerized tomography (CT) scans of thermoplastic polyamide printed parts, it was found that both agents yielded some degree of porosity. Interestingly, the sodium bicarbonate pore-promoting agent (see pores 720 in FIG. 7B) yielded higher pore density that could be attributed to the lower decomposition temperature of sodium bicarbonate when compared to urea (see pores 710 in FIG. 7A).

Definitions

It is noted that, as used in this specification and the appended claims, the singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise.

As used herein, “colorant” can include dyes and/or pigments.

As used herein, “dye” refers to compounds or molecules that absorb electromagnetic radiation or certain wavelengths thereof. Dyes can impart a visible color to an ink if the dyes absorb wavelengths in the visible spectrum.

As used herein, “pigment” generally includes pigment colorants, magnetic particles, aluminas, silicas, and/or other ceramics, organo-metallics or other opaque particles, whether or not such particulates impart color. Thus, though the present description primarily exemplifies the use of pigment colorants, the term “pigment” can be used more generally to describe pigment colorants, and also other pigments such as organometallics, ferrites, ceramics, etc. In one specific aspect, however, the pigment is a pigment colorant.

As used herein, “ink jetting” or “jetting” refers to compositions that are ejected from jetting architecture, such as ink-jet architecture. Ink-jet architecture can include thermal or piezo architecture. Additionally, such architecture can be configured to print varying drop sizes such as less than 10 picoliters, less than 20 picoliters, less than 30 picoliters, less than 40 picoliters, less than 50 picoliters, etc.

As used herein, “average particle size” refers to a number average of the diameter of the particles for spherical particles, or a number average of the volume equivalent sphere diameter for non-spherical particles. The volume equivalent sphere diameter is the diameter of a sphere having the same volume as the particle. Average particle size can be measured using a particle analyzer such as the Mastersizer™ 3000 available from Malvern Panalytical. The particle analyzer can measure particle size using laser diffraction. A laser beam can pass through a sample of particles and the angular variation in intensity of light scattered by the particles can be measured. Larger particles scatter light at smaller angles, while small particles scatter light at larger angles. The particle analyzer can then analyze the angular scattering data to calculate the size of the particles using the Mie theory of light scattering. The particle size can be reported as a volume equivalent sphere diameter.

As used herein, the term “substantial” or substantially when used in reference to a quantity or amount of a material, or a specific characteristic thereof, refers to an amount that is sufficient to provide an effect that the material or characteristic was intended to provide. The exact degree of deviation allowable may in some cases depend on the specific context. When using the term “substantial” or “substantially” in the negative, e.g., substantially devoid of a material, what is meant is from none of that material is present, or at most, trace amounts could be present at a concentration that would not impact the function or properties of the composition as a whole.

As used herein, the term “about” is used to provide flexibility to a numerical range endpoint by providing that a given value may be “a little above” or “a little below” the endpoint. The degree of flexibility of this term can be dictated by the particular variable and determined based on the associated description herein.

As used herein, a plurality of items, structural elements, compositional elements, and/or materials may be presented in a common list for convenience. However, these lists should be construed as though individual members of the list is individually identified as a separate and unique member. Thus, no individual member of such list should be construed as a de facto equivalent of any other member of the same list solely based on their presentation in a common group without indications to the contrary.

Concentrations, amounts, and other numerical data may be expressed or presented herein in a range format. It is to be understood that such a range format is used merely for convenience and brevity and thus should be interpreted flexibly to include the numerical values explicitly recited as the limits of the range, and also to include individual numerical values or sub-ranges encompassed within that range as if a numerical value and sub-range is explicitly recited. As an illustration, a numerical range of “about 1 wt % to about 5 wt %” should be interpreted to include the explicitly recited values of about 1 wt % to about 5 wt %, and also to include individual values and sub-ranges within the indicated range. Thus, included in this numerical range are individual values such as 2, 3.5, and 4 and sub-ranges such as from 1-3, from 2-4, and from 3-5, etc. This same principle applies to ranges reciting a single numerical value. Furthermore, such an interpretation should apply regardless of the breadth of the range or the characteristics being described. 

What is claimed is:
 1. A multi-fluid kit for three-dimensional printing comprising: a fusing agent comprising water and a radiation absorber, wherein the radiation absorber absorbs radiation energy and converts the radiation energy to heat; and a pore-promoting agent comprising water and a water-soluble pore-promoting compound, wherein the pore-promoting compound chemically reacts at an elevated temperature to generate a gas, and wherein the water-soluble pore-promoting compound is selected from the group consisting of sodium bicarbonate, potassium bicarbonate, and combinations thereof.
 2. The multi-fluid kit of claim 1, wherein the pore-promoting compound is sodium bicarbonate.
 3. The multi-fluid kit of claim 1, wherein the pore-promoting compound is present in an amount from about 1 wt % to about 10 wt % with respect to the total weight of the pore-promoting agent.
 4. The multi-fluid kit of claim 1, wherein the elevated temperature at which the pore-promoting compound chemically reacts is from about 80° C. to about 200° C.
 5. The multi-fluid kit of claim 1, wherein the radiation absorber is a metal dithiolene complex, carbon black, a near-infrared absorbing dye, a near-infrared absorbing pigment, metal nanoparticles, a conjugated polymer, or a combination thereof.
 6. The multi-fluid kit of claim 1, further comprising a detailing agent comprising a detailing compound, wherein the detailing compound reduces a temperature of powder bed material onto which the detailing agent is applied.
 7. A three-dimensional printing kit comprising: a powder bed material comprising polymer particles; a fusing agent comprising water and a radiation absorber to selectively apply to the powder bed material, wherein the radiation absorber absorbs radiation energy and converts the radiation energy to heat; and a pore-promoting agent comprising water and a water-soluble pore-promoting compound, wherein the pore-promoting compound chemically reacts at an elevated temperature to generate a gas, and wherein the water-soluble pore-promoting compound is selected from the group consisting of sodium bicarbonate, potassium bicarbonate, and combinations thereof.
 8. The three-dimensional printing kit of claim 7, wherein the polymer particles have an average particle size from about 20 μm to about 100 μm and include polyamide-6, polyamide-9, polyamide-11, polyamide-12, polyamide-6,6, polyamide-6,12, polyethylene, thermoplastic polyurethane, thermoplastic polyamide, polypropylene, polyester, polycarbonate, polyether ketone, polyacrylate, polystyrene powder, wax, or a combination thereof.
 9. The three-dimensional printing kit of claim 7, wherein the pore-promoting compound is sodium bicarbonate.
 10. The three-dimensional printing kit of claim 7, wherein the radiation absorber is a metal dithiolene complex, carbon black, a near-infrared absorbing dye, a near-infrared absorbing pigment, metal nanoparticles, a conjugated polymer, or a combination thereof.
 11. The three-dimensional printing kit of claim 7, wherein the elevated temperature at which the pore-promoting compound chemically reacts is from about 80° C. to about 200° C.
 12. A method of three-dimensional printing comprising: iteratively applying individual build material layers of polymer particles to a powder bed; based on a three-dimensional object model, selectively jetting a fusing agent onto the individual build material layers, wherein the fusing agent comprises water and a radiation absorber; based on the three-dimensional object model selectively jetting a pore-promoting agent onto the individual build material layers, wherein the pore-promoting agent comprises water and a water-soluble pore-promoting compound, wherein the pore-promoting compound chemically reacts at an elevated temperature to generate a gas, and wherein the water-soluble pore-promoting compound is selected from the group consisting of sodium bicarbonate, potassium bicarbonate, and combinations thereof; and exposing the powder bed to energy to selectively fuse the polymer particles in contact with the radiation absorber to form a fused polymer matrix at individual build material layers, thereby heating the pore-promoting compound to the elevated temperature to generate the gas distributed in the fused polymer matrix.
 13. The method of claim 12, wherein the pore-promoting compound is sodium bicarbonate.
 14. The method of claim 12, wherein the elevated temperature is from about 80° C. to about 200° C.
 15. The method of claim 12, wherein the gas forms isolated pores in the fused polymer matrix, the pores having an average diameter from about 0.1 micrometer to about 100 micrometers. 